| Prouduct Code | GLUEFILM-250 | GLUEFILM-125 |
| Specifications | Prepreg Weight: 250 GSM (±35) | Prepreg Weight: 125 GSM (±18) |
| Thickness: 0.20±0.01 | Thickness: 0.10±0.01 | |
| Resin content: 90% | Resin content: 85% | |
| Fiberglass content: 20 GSM | Fiberglass content: 20 GSM |
Cure Cycle and Tg
105~115°C achieved after 240min curing @ 90°C
120~130°C achieved after 40min curing @ 130°C
120~130°C achieved after 10min curing @ 150°C
Out of autoclave curing
Vacuum shouldn’t not be less than -0.085Mpa and rate of heating should be 1-3°C/minute. For ideal curing, hold for 60 minutes at 130°C. Avoid rapid cooling.
Autoclave Curing
Vacuum shouldn’t not be less than -0.085Mpa, pressure should be 1-3 bar and rate of heating should be 1-3°C/minute. For ideal curing, hold for 60 minutes at 130°C. Avoid rapid cooling.
Storage
30 days @ 23°C
12 months @ -18°C
Features
• Strong bonding strength
• Service temperature up to 150°C
• Easy handling and long lasting (1 month out-life at room temperature and a year at -18°C)
• Reduced shrinkage and low CTE
• Compatible with our carbon, Kevlar and fiberglass prepregs
• Flame-retarded version of the same adhesive film also available.
For alternatives on curing cycle, please contact us.