Advantages of using multiaxial Carbon fabric
- Because the fibres are always straight and non-crimped and also the fact that several orientations(0°, 45°, 90°) of fibres are possible on one fabric, these multiaxial fabrics are able to offer the maximum mechanical strength.
- Since Multiaxial fabrics are thicker and with multiple fibre orientations, fewer layers are needed to build a laminate. This results in a faster building speed and saving labor costs as well
Multiaxial carbon fiber fabrics detail specifications
| Product No. | Material | Stitching type & fiber orientation | Fabric Weight (g/m2） | 0°Layer | +45°Layer | +90°Layer | -45°Layer（g/m2） | Polyester Yarn | Standard Width |
| Type | （g/m2） | （g/m2） | （g/m2） | (g/m2） | (m) | ||||
| CABX200 | Carbon 12K/24K | Biaxial +45°/ -45° | 206 | / | 100 | / | 100 | 6 | 1.27 |
| CABX300 | Carbon 12K/24K | Biaxial +45°/ -45° | 306 | / | 150 | / | 150 | 6 | 1.27 |
| CABX400 | Carbon 12K/24K | Biaxial +45°/ -45° | 406 | / | 200 | / | 200 | 6 | 1.27 |
| CABX600 | Carbon 12K/24K | Biaxial +45°/ -45° | 606 | / | 300 | / | 300 | 6 | 1.27 |
| CALT300 | Carbon 12K/24K | LT Biaxial 0°/90° | 306 | 150 | / | 150 | / | 6 | 1.27 |
| CALT400 | Carbon 12K/24K | LT Biaxial 0°/90° | 406 | 200 | / | 200 | / | 6 | 1.27 |
| CALT600 | Carbon 12K/24K | LT Biaxial 0°/90° | 606 | 300 | / | 300 | / | 6 | 1.27 |
| CATX300-A | Carbon 12K/24K | Triaxial +45°/ -45°/ 0° | 306 | 100 | 100 | 100 | / | 6 | 1.27 |
| CATX300-B | Carbon 12K/24K | Triaxial 90°/ 0°/ 90° | 306 | 100 | / | 200 | / | 6 | 1.27 |
| CAQX600 | Carbon 12K/24K | Quadriaxial | 606 | 150 | 150 | 150 | 150 | 6 | 1.27 |
| CAQX800 | Carbon 12K/24K | Quadriaxial | 806 | 200 | 200 | 200 | 200 | 6 | 1.27 |
All the above multiaxial fabrics are produced using 12K or 24k fibers.
All these fabrics are 1.27 meter in width; Each roll is 50/100 meters
Fiber brands can be Toray, Formosa, Dowaksa, Mitsubishi depending on your requirement